Eroded enamel rehardening using two intraoral appliances designs in different times of salivary exposure.
2019
Background The aim of this study was evaluated the eroded enamel rehardening potential using upper palatal and lower buccal removable appliances in different times of salivary exposure (30 min, 1h, 2h, 12h) after a single erosive challenge event. Material and Methods After initial surface hardness evaluation, bovine enamel blocks were eroded in vitro (0.01 M hydrochloric acid, pH 2.3, 30 seconds), selected (n = 160) and randomly assigned to the two appliance designs and twenty volunteers. Four enamel blocks were inserted in each removable appliance. On the in situ phase, the volunteers were instructed to use the upper palatal and lower buccal appliances simultaneously for 12 nonconsecutive …
A zinc-doped endodontic cement facilitates functional mineralization and stress dissipation at the dentin surface
2018
Objective: The purpose of this study was to evaluate nanohardness and viscoelastic behavior of dentin surfaces treated with two canal sealer cements for dentin remineralization. Material and Methods: Dentin surfaces were subjected to: i) 37% phosphoric acid (PA) or ii) 0.5 M ethylenediaminetetraacetic acid (EDTA) conditioning prior to the application of two experimental hydroxyapatite-based cements, containing sodium hydroxide (calcypatite) or zinc oxide (oxipatite), respectively. Samples were stored in simulated body fluid during 24 h or 21 d. The intertubular and peritubular dentin were evaluated using a nanoindenter to assess nanohardness (Hi). The load/displacement responses were used f…
Strukturelle Veränderungen in säuregeätztem Schmelz im konfokalen Laser-Scanning-Mikroskop
1996
The aim of the present investigation was to elucidate structural alternations in enamel subjected to acid etch technique and treatment under remineralizing conditions by means of a new microscopy technique known as confocal laser scanning microscopy (CLSM). Blocks of enamel were treated with 37% phosphoric acid and exposed for 3 weeks to an oral environment. Tomographic CLSM images were subsequently obtained and compared with controls. CLSM proved to be a reliable, highly reproducible and simple method of qualitative assessment of structural changes occurring on the surface of enamel and in areas below the surface as deep as 100 microns or more. Structural alterations associated with acid a…
Remineralization effects of conventional and experimental ion-releasing materials in chemically or bacterially-induced dentin caries lesions
2019
Abstract Objectives The aim of this study was to evaluate the remineralization effects of conventional and experimental ion-releasing materials on different artificial dentin carious lesions. Methods Forty human dentin discs were submitted to different demineralization protocols for simulated caries lesion: (D1) Shallow chemically-induced caries, (D2) deep chemically-induced caries, (D3) deep bacterially-induced caries. Each disc was divided in five parts; one of those served as baseline control. The remaining parts of each disc (n = 12–16/group) were treated using the following materials: EXP, an experimental resin-based bioactive material consisting of a self-etch primer and an adhesive c…
Comparative evaluation of bioactive cements on biomimetic remineralization of dentin
2020
Background This study was designed to quantitatively compare the presence of apatite peaks on demineralized dentin to induced bio-mimetically by bioactive commercial materials. Material and methods Dentin slice specimens (n=6) were prepared and demineralized by by17% EDTA for 2 hours. Each disks materials (Theracal, Biodentine, CPP-ACP) were freshly prepared and was maintained in close contact with a demineralized dentin specimen immersed in PBS solution during one week. To evaluation of bioactivity, cements disks (n=6) were prepared from each material and immersed in PBS solution for one week. The bioactivity and remineralization ability was evaluated using FTIR spectroscopy and Scanning E…
Enamel remineralization and surface roughness after treatment with herbal-containing toothpastes
2021
Background Oral care products containing bioactive agents obtained from extracts of plant drugs were launched. This in vitro study investigated the effects of herbal-containing toothpastes associated or not with fluoride to remineralize the enamel after cariogenic challenge with pH cycling. The chemical and physical factors of toothpastes and the enamel surface roughness after brushing were also analyzed. Material and methods Sixty bovine enamel blocks were obtained and divided into 3 thirds: intact (untreated), demineralized (artificial caries lesion), and treated (caries lesion, pH cycling, and brushing with toothpastes). Toothpastes containing herbal compounds contained no fluoride [Gall…
Silver-loaded nanoparticles affect ex-vivo mechanical behavior and mineralization of dentin
2019
Background: The aim was to evaluate the effect of silver loaded nanoparticles (NPs) application on the triboscopic, crystallographic and viscoelastic properties of demineralized dentin. Polymethylmetacrylate-based NPs and Ag loaded NPs were applied on demineralized dentin. Material and Methods: Treated and untreated surfaces were probed by a nanoindenter to test viscoelasticity, and by atomic force microscopy to test nanoroughness and collagen fibril diameter. X-ray diffraction and transmission electron microscopy through selected area diffraction and bright-field imaging were also used. Results: Dentin treated with Ag-NPs attained the lowest complex modulus, and the highest tan delta value…
Effect of application time and concentration of silver diamine fluoride on the enamel remineralization
2021
Background Silver diamine fluoride has attracted attention because of its clinical success in arresting dental caries. Thus, the aim of this study was to evaluate the effect of different application times and concentrations of silver diamine fluoride (SDF) on deciduous tooth enamel remineralization. Material and Methods Blocks of deciduous tooth enamel were categorized into six groups of 11 each: 2 control groups: intact enamel, and demineralized enamel; 38% SDF and 30% SDF which were subdivided according to application times (1 and 3 min). The microhardness of samples was determined, and all groups except the intact enamel group were subjected to pH cycling to produce initial carious lesio…